Fracturing behavior of process pipelines, which transport corrosive hydrocarbons of high parameters

UDK: 622.692.4.004.6
DOI: 10.24887/0028-2448-2022-7-136-139
Key words: process pipeline, steel 09G2S, nonrotational pipe weld joints, corrosion-erosion wear, corrosion cracking
Authors: E.E. Zorin (The Pipeline Transport Institute LLC, RF, Moscow), D.V. Derkach (The Pipeline Transport Institute LLC, RF, Moscow), V.G. Pirozhkov (Gubkin University, RF, Moscow)

When developing new hydrocarbon deposits in old fields, problems related to providing operational reliability of process pipelines built using conventional steels and technologies, which were used for this climatic zone, and formerly known characteristics of recovered hydrocarbons, occur increasingly. It was found that one of the reasons of premature failure of new transport networks consists in difference between existing operational conditions and parameters laid in the design, based on which materials and technologies for oil field development were selected. These unconsidered differences were realized in pipelines from steel 09G2S as a synergistic effect, which resulted in sharp increase of corrosion and erosion damage rates for pipes themselves, various pipeline structural elements (connecting parts), as well as their weld joints. In conditions of high flow rates of gas-condensate mixture with variable density, stable turbulent motion is formed in a pipeline system, which results in rill-washing corrosion in pipes, that is increased with carbon dioxide corrosion; at that flow breakaway in metal “leak” areas in root sections of nonrotational ring erection joints or sharp change of flow motion angle in branch sleeves and elbow bends by 900 results in increase of corrosion-erosion wear, intensity of which starts depending directly on corrosion and mechanical characteristics of the base metal, weld joint areas metal, level of residual welding stresses; in single pipeline areas it could reach 3-4 mm/year. The paper shows mechanisms of corrosion-erosion failure of steel 09G2S and its weld joints, as well as it presents recommendations on performability increase for process pipelines under these operational conditions.


1. Heidersbach R., Metallurgy and corrosion control in oil and gas production, Wiley, 2011, 281 p.

2. Vnutrennyaya korroziya i zashchita truboprovodov na mestorozhdeniyakh Zapadnoy Sibiri (Internal corrosion and protection of pipelines in the fields of Western Siberia), Moscow: Nedra Publ., 1997, 379 p.

3. Zorin E.E., Stepanenko A.I., Resistance to destruction of technological pipelines made of steel type 09G2S during thermal cycling in the climatic temperature range (In Russ.), Gazovaya promyshlennost’, 1994, no. 2, pp. 22–23.

4. Basiev K.D., Zorin E.E., Steklov O.I., Corrosion resistance of welded casing pipes (In Russ.), Avtomaticheskaya svarka, 1987, no. 8, pp. 48–51.

5.  Neganov D.A., Zorin E.E., Zorin N.E., Assessment of influence of surface crack-like stress concentrators on main pipeline operability (In Russ.), Nauka i tehnologii truboprovodnogo transporta nefti i nefteproduktov = Science & Technologies: Oil and Oil Products Pipeline Transportation, 2021, V. 11, no. 1, pp. 8–15, DOI:

6. Zorin E.E., Pirozhkov V.G., K voprosu prognozirovaniya resursa ekspluatatsii tonkostennykh obolochkovykh konstruktsiy iz plastichnykh staley (On the issue of predicting the service life of thin-walled shell structures made of ductile steels), Collected papers “Magistral’nye i promyslovye truboprovody: proektirovanie, stroitel’stvo, ekspluatatsiya, remont” (Main and field pipelines: design, construction, operation, repair), 2000, no. 3, pp. 24–25.

Zorin E.E., Lanchakov G.A., Pashkov Yu.I., Stepanenko A.I., Rabotosposobnost’
truboprovodov (Pipeline performance), Part 2. Soprotivlyaemost’ razrusheniyu
(Destruction resistance), Moscow: Nedra Publ., 2001, 350 p.

To buy the complete text of article (a format - PDF) or to read the material which is in open access only the authorized visitors of the website can. .

Mobile applications

Read our magazine on mobile devices

Загрузить в Google play

Press Releases